SHP Graphite Electrode

Needle coke and pitch are mixed as per proportion and then molded. Heat treatment is then applied in the baking and graphitization process to form the finished product.

  • Product Details

Physical & Chemical Properties of SHP Graphite Electrodes

Items

Classification

Unit

Nominal Diameter (mm)

300-400

450-600

Resistivity

Electrode

μΩm

6.5

6.5

Nipple

5.5

5.5

Bending Strength

Electrode

Mpa

10.0

10.0

Nipple

18.0

18.0

Young’s Modulus

Electrode

Gpa

14.0

14.0

Nipple

18.0

18.0

Bulk Density

Electrode

g/cm3

1.64

1.63

Nipple

1.72

1.72

CTE100℃-600℃

Electrode

×10-6/℃

2.2

2.2

Nipple

1.6

1.6

Ash Content

Electrode

%

0.3

0.3

Nipple

Note: Ash Content is only for reference. 


Recommended current load of SHP Graphite Electrodes

Grade

Nominal Dia.

Allowable current  A

Current density  A/cm2

SHP electrode

300mm

1400020000

1928

350mm

1800026000

1827

400mm

2300033000

1826

450mm

2700042000

1726

500mm

3400052000

1726

550mm

4000060000

1624

600mm

4500070000

1624


Related Products
  • UHP Graphite Electrode UHP Graphite Electrode Physical & Chemical Properties of UHP Graphite Electrodes...
  • Graphite Electrode Graphite Electrode Graphite Electrode Soldering Iron Graphite electrode is nothing more than a sharp...
  • Carbon Electrode Carbon Electrode Carbon electrode are applied for the production of silicon metal as they have peculiar...

Contact

Graphite Electrode:  

Tel & WhatsApp & Wechat:    +86 18832836236

Email:  tingy.yu@orientcarbongraphite.com


Soderberg Electrode Paste, Carburiser:  

Tel & WhatsApp & Wechat:    +86 13932852502

Email:  marketing@orientcarbongraphite.com


Cathode block, Pre-baked Anode Block

Tel & WhatsApp & Wechat:    +86 13932852502

Email:  marketing@orientcarbongraphite.com

Website: www.orientcarbongraphite.com

facebook twitter google+ linkedin printerest